PENGARUH PERLAKUAN PELAPISAN UJUNG TERHADAP PENGURAN GAN PECAH PADA PATUNG KA YU (BAGIAN I)

Jamal Balfas

Abstract


Physical deformation such as checks or cracks is commonly encountered in the process of drying wood statues.  In the senses of economic and quality improvement, such a case has long been a serious handicap to the Balinese crofters.  A number of trials have been made through modification of drying schedules, but these gave  little protection agents check/crack development, particularly for the medium  to  large size  statues. The  use of polyethylene glycol  (PEG-1000) has significantly  reduced  the  rate  of physical deformation, however, it raised another problem  in finishing and could promote a surface  discoloration. This study  examined another approach of cracking prevention by application of coating treatments to the end grain of wood structure.

Fresh  logs of  two  wood species,  i.e., sengon  (Paraserianthes  falcataria  {L.)  Nielsen.)  and  mindi  (Melia azedarach  L.)  were crosscut to 50 cm long specimens,  and then shaped into a simple cat-form statues sizing of approximately  21 cm  wide and 46 cm long. End coatings were applied separately using 4 different materials, i.e., resorcinol formaldehyde, polyvinyl acetate, wood filler and cement.  All treatments were accomplished approximately 30 minutes prior to oven drying, Physical deformation of wood statues was de/ermined  by measuring the width,  length and gap-size of cracks using a digital caliper. The related physical characteristics, such as moisture content and specific: gravity of each species were also determined.

Sengon  had a lower  specific: gravity, but a  greater  green  moisture  content  and  dry-ability  than  mindi. Wood physical deformation of both treated and untreated sengon was obviously greater than mindi.   The effectiveness of end coating treatments in reducing  wood cracks  varied according  twood species  and the coating materials.     Wood statues  of sengon  experienced more rigorous cracks than those of mindi.   The  use of wood adhesives as coating materials gave a helter cracking protection than the wood filling agents. Although polyvinyl acetate could not greatly minimize the physical deformation  of belalu,  it revealed  to be the most effective coating material for cracking prevention.

 


References


Gallagher, L.1989. Principles of moisture movement. Asean mobile workshop on wood drying. Asean Timber Technology Centre, Malaysia.

Haygreen, J.G., and J.L. Bowyer. 1985. Forest products and wood science. The Iowa State University Press, Ames.

Lembaga Penelitian Hasil Hutan. 1979. Penelitian pengeringan patung kayu Bali. Laporan dalam rangka kerjasama Badan Pengembangan Ekspor Nasional dan Lembaga Penelitian Hasil Hutan Bogor. Tidak diterbitkan.

Mustafa, Z. 1994. Panduan microstat untuk mengolah data statistik. Edisi III. Andi Offset,Yogyakarta.

Nandika, D., dan l.K. Suardika. 1993. Masalah kerusakan patung kayu di propinsi Bali. Seminar sehari dalam rangka "Peningkatan kualitas patung Bali melalui proses pengawetan dan pengeringan kayu". Kerjasama Kanwil Departemen Perindustrian dan APKIN. Tidak diterbitkan.

Suardika, l.K. I 991. Kerusakan patung kayu akibat faktor biologis di Kabupaten Gianyar, Bali. Skripsi Fakultas Kehutanan IPB, Bogor. Tidak diterbitkan.

Subramanian, R.V. 1984. Chemistry of adhesion. American Chemical Society, Washington D.C..




DOI: https://doi.org/10.20886/jphh.1994.12.5.169%20-174

Refbacks

  • There are currently no refbacks.


JURNAL PENELITIAN HASIL HUTAN INDEXED BY:

More...


Copyright © 2015 | Jurnal Penelitian Hasil Hutan (JPHH, Journal of Forest Products Research)
eISSN : 2442-8957, pISSN : 0216-4329
JPHH is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.